The crack propagation resistance for alloy 8090 sheet decreases with the increase of content of Na and K impurities.An improvement over the fracture toughness and crack initiation resist- ance for the alloy containing Na and K within certain limit may be made by adding 0.05% Ce.This beneficial modification would not be manifested if the alloy contained more Na and K.One of the reasons why Na and K injure the toughness of the alloy might be due to that they cause the precipitation of T_1 phase along grain and subgrain boundaries and accelerate the abnormal growth of recystallized grains.
关键词:
alloy 8090
,
null
,
null
,
null
,
null
LIU Yulin ZHANG Yun ZHAO Hong'en HU Zhuangqi SHI Changxu Institute of Metal Research
,
Academia Sinica
,
Shenyang
,
China Associate Professor
,
Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
China
金属学报(英文版)
The solid-liquid interface morphology and solute segregation behaviour of AI-Li alloy 8090 during unidirectional solidification were studied by the liquid metal quenehing method under varied processing conditions.When solidification rate,RO.75 mm/min (temper- ature gradient,G_L=130℃/cm),the structure revealed of planar or dendritic interface respectively.With the increase of R,the interface morphology becomes cellular from planar gradually,within a narrow range.And the greater the R,the,finer the dendrite.Segregation of element Cu and impurity elements Fe and Si are quite severe,the interface morphology markedly influences on solute segregation.During solidification at coarse dendrite interface, their segregation ratios are rather great and solidified structure is coarse.
关键词:
Al-Li alloy
,
null
,
null
,
null
,
null
孟亮
,
张宝昌
,
梁英
,
张卫中
,
田普科
金属学报
研究了含0.05％Ce及不同Na,K杂质含量的8090合金薄板裂纹扩展阻力,探讨了合金断裂韧性及裂纹起始扩展阻力随(Na+K)含量变化的规律和微量Ce的作用,结果指出:随(Na+K)含量增加,合金裂纹扩展阻力下降;若(Na+K)含量处于一定范围内时,合金中加入0.05％Ce会改善其断裂韧性及裂纹起始扩展抗力;当(Na+K)含量过高,Ce的这种有益作用便被掩盖,Na,K对合金韧性造成危害的原因之一是可以促使T_1等相沿晶界或亚晶界析出,并促使再结晶晶粒异常长大。
关键词:
Al-Li合金
,
crack propagation resistance
,
Ce
,
fracture toughness
,
alkali metal
SUN Dongsheng LI Fengzhao ZHANG Gang Shandong Polytechnic University
,
Jinan
,
China Lecturer
,
Centre of Materials Testing and Analysis
,
Shandong Polytechnic University
,
Jinan 250014
,
China
金属学报(英文版)
Cryogenic strength,ductility and toughness of AI-Li alloy 8090 were found to be superior to those at ambient temperature,and up to optima at about 20 K.Different aging regimes may only influence on its cryogenic yield strength and elongation.
关键词:
Al-Li alloy
,
null
,
null
,
null